SSAB Multisteel SNL

Download data sheet

General Product Description

Normalized structural steel heavy plate.

SSAB Multisteel SNL is hot rolled structural steel for general steel constructions. SNL = Structural Normalized Low Temperature.

Exceeding the requirements of several standard steel grades, SSAB Multisteel SNL is a versatile structural steel for fabricated products and steel frame structures. Formability and highly consistent quality guarantee fast, uninterrupted production, generating clear savings in the costs of material management.

SSAB Multisteel SNL exceeds several steel standards and is available as six standard steel grades: S355N and S355NL according to EN 10025-3 and S355K2+N, S355J2+N, S355J0+N and S355JR+N according to EN 10025-2.

CE marking:

SSAB Raahe Works is authorized to use the CE marking for structural steels according to EN 10025-2 and EN 10025-3 based on EN 10025-1.

The CE marking is marked on an extra page of inspection certification 3.1.

Dimension Range

SSAB Multisteel SNL is available in thickness of 5.00 - 150.00 mm.

Mechanical Properties

Thickness
(mmin)
Thickness
(mmin)
5.00 - 16.000.197 - 0.6299
Yield strength
(min MPa)
355
Tensile strength
(MPa)
470 - 630
Elongation A5
(min %)
22
Thickness
(mmin)
Thickness
(mmin)
16.01 - 40.000.6303 - 1.575
Yield strength
(min MPa)
345
Tensile strength
(MPa)
470 - 630
Elongation A5
(min %)
22
Thickness
(mmin)
Thickness
(mmin)
40.01 - 63.001.575 - 2.480
Yield strength
(min MPa)
335
Tensile strength
(MPa)
470 - 630
Elongation A5
(min %)
22
Thickness
(mmin)
Thickness
(mmin)
63.01 - 80.002.481 - 3.150
Yield strength
(min MPa)
325
Tensile strength
(MPa)
470 - 630
Elongation A5
(min %)
21
Thickness
(mmin)
Thickness
(mmin)
80.01 - 100.003.150 - 3.9370
Yield strength
(min MPa)
315
Tensile strength
(MPa)
470 - 630
Elongation A5
(min %)
21
Thickness
(mmin)
Thickness
(mmin)
100.01 - 150.003.9374 - 5.9055
Yield strength
(min MPa)
295
Tensile strength
(MPa)
450 - 600
Elongation A5
(min %)
21

The mechanical properties are tested transverse to the direction of rolling.

Impact Properties

SSAB Multisteel SNL

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
27 J / -50 °C

EN 10025-3 S355NL

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
27 J / -50 °C

EN 10025-3 S355N

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
40 J / -20 °C

EN 10025-2 S355K2+N

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
40 J / -20 °C

EN 10025-2 S355J2+N

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
27 J / -20 °C

EN 10025-2 S355J0+N

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
27 J / 0 °C

EN 10025-2 S355JR+N

Min. impact energy for longitudinal testing,
Charpy V 10x10 mm test specimens
J / °C

The impact test is made longitudinal to the rolling direction in compliance with EN 10025-1 and EN 10025-2.

Chemical Composition (ladle analysis)

C
(max %)
C
(max %)
0.18
Si
(max %)
0.50
Mn
(max %)
1.60
P
(max %)
0.020
S
(max %)
0.010
Nb
(max %)
0.05

Carbon Equivalent CEV

Thickness (mmin)
Thickness (mmin)
CEV (max %)
5.00 - 63.000.197 - 2.480
0.43
63.01 - 150.002.481 - 5.9055
0.45

Tolerances

Thickness ¾ from EN 10029 Class A.

Width and length according to EN 10029.

Flatness tolerance 4 mm/m.

Surface according to EN 10163-2 Class A subclass 1.

Delivery Conditions

Normalized.

Coating

Shot blasted & primed surface is available upon request.

Certificates

SSAB Multisteel SNL provides three different certificates:

EN 10204-3.1 to SSAB Multisteel SNL.

EN 10204-3.1 +CE to S355NL/N EN 10025-3.

EN 10204-3.1 +CE to S355K2/J2/J0/JR+N EN 10025-2.

Fabrication and Other Recommendations

Welding:

Weldability is excellent with all welding processes. Increased working temperature requirements are less than those of the corresponding strength grades of standard steels. This means easier welding and cost savings under both workshop and site welding conditions.

Needed working temperatures for thick plates please consult SSAB Tech Support.

Forming:

SSAB Multisteel offers better formability properties than standard steels. Successful forming requires that the manufacturer uses good workshop techniques. Worn tools, poor lubrication, scratches on the surface of the steel as well as edge burrs will all reduce forming quality.

Guaranteed minimum bending radius for all directions is 1.5 x t up to 30 mm thick plate where t = plate thickness.

Heat treatment:

Recommendations for stress relieving and normalizing

Stress relieving 550 – 600°C (target 580°C)

2 minutes/millimeter of thickness, however, 30 minutes minimum. Slow cooling in the furnace.

Normalizing 900 – 940°C (target 920°C)

1 minute/millimeter of thickness, however, 20 minutes minimum. Cooling in free air.

For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.